MIM-LD-G19
MIM LD-G19 is Jingye Lide's proprietary ultra-high-strength maraging steel. Based on a carbon-free (or micro-carbon) martensitic matrix, it achieves strengthening through age-hardening precipitation of intermetallic compounds. The tensile strength exceeds 2000 MPa after post-heat-treatment, which makes it one of the highest-strength grade among MIM materials at present. And it is designed for aerospace, high-end equipment, and applications demanding extreme strength.
Product Specifications
Chemical Composition (wt%)
|
C |
Cr |
Ni |
Mo |
Co |
Nb |
Si |
Mn |
Fe |
|
＜0.03 |
7.0-9.0 |
4.5-7.0 |
5.0-7.0 |
15.0-17.0 |
＜0.5 |
＜0.5 |
＜0.5 |
Bal. |
Physical Properties
|
Item |
Value |
|
Tap Density |
≥4.4 g/cm³ |
|
Apparent Density |
≥2.8 g/cm³ |
|
D10 |
2.0-3.0 μm |
|
D50 |
6.0-8.0 μm |
|
D90 |
15-18 μm |
Sintered Part Properties
|
Property |
As-Sintered |
Heat-Treated (Spec) |
Typical |
|
Density (g/cm³) |
≥7.8 |
— |
— |
|
Tensile Strength (MPa) |
900-1000 |
≥2000 |
2150 |
|
Yield Strength (MPa) |
650-750 |
≥1900 |
1950 |
|
Elongation (%) |
10-13 |
≥5 |
6.0 |
|
Hardness (HRC) |
25-30 |
≥50 |
53 |
Recommended Heat Treatment: 1070℃-1100℃ × 2.5h Solution Treatment → 530℃-550℃ × 4h Aging
Recommended Heat Treatment: 1070℃ -1100℃× 2.5h solution → 530℃-550℃ × 4h aging
Typical Applications
Aerospace precision structural components
High-end defense equipment parts
Motorsport & high-performance automotive parts
Industrial parts requiring extreme strength
Product Photos
Have Questions About Your Project?
Contact our experts for support with material selection, product development, additive manufacturing and process optimization.
Let us help you with your project.
Navigation
Navigation
Contact Us
Tel.: +86 0311 8289 8906 / +86 150 3207 1231
E-mail: jyzczz@hbjyjt.com
Fax: +86 311 8289 8906
Address: Jingye Industrial Park, Nandian Town, Pingshan County, Shijiazhuang City, Hebei Province, China